This 304 stainless steel stock sheet offers superior corrosion resistance and mechanical strength, making it ideal for critical hydraulic system components. Engineered for longevity in harsh environments.
| Standard | ASME B18 |
| Material | 304 Stainless Steel |
| Finish | Black Oxide |
| Grade | N/A |
| Thickness | 0.404" |
| Length | 33" |
| Width | 35" |
A proven choice for industrial professionals, this 0.404-inch thick, 33-inch by 35-inch 304 stainless steel stock sheet provides exceptional performance in hydraulic applications. The inherent corrosion resistance of 304 stainless steel, characterized by its chromium and nickel content, ensures integrity against aggressive fluids and environmental factors. Its robust mechanical properties, including good tensile strength and formability, allow for precise fabrication of manifold blocks, pressure vessels, and structural components within hydraulic systems, guaranteeing reliability and extended service life under demanding operational conditions.
This component strictly adheres to the tolerances, material specifications, and quality benchmarks set by the world's leading industrial manufacturers.
1. Clean the sheet surface thoroughly to remove any contaminants. 2. Precisely cut the sheet to the required dimensions using appropriate cutting tools for stainless steel. 3. Fabricate the component according to design specifications, ensuring all welds and connections meet hydraulic pressure standards.
| Standard System | Designation |
|---|---|
| ISO Equivalent | ISO 9001:2015 Mfg |
| DIN Equivalent | Industry Standard |
| Primary Standard | ASME B18 |
| Tensile Strength | 75,000 psi (515 MPa) |
| Yield Strength | 30,000 psi (205 MPa) |
| Elongation in 2 in. | 40% min |
| Hardness | Rockwell B95 max |
| Carbon (C) | 0.08% max |
| Chromium (Cr) | 18.0 - 20.0% |
| Nickel (Ni) | 8.0 - 10.5% |
| Manganese (Mn) | 2.00% max |
| Size / Type | Est. Weight (lbs/100) | Shipping Weight (kg) |
|---|---|---|
| Standard | Varies by dimension | Contact Sales |
| Environment | Rating |
|---|---|
| Indoor / Dry | Excellent |
| Outdoor / Exposed | Excellent |
| Marine / Saltwater | Good |
| Chemical / Acidic | Not Recommended |
| ❌ Mistake | ✅ Correct Approach |
|---|---|
| Using standard carbon steel in corrosive hydraulic environments. | Always specify 304 or 316 stainless steel for hydraulic components exposed to corrosive fluids or environments to prevent premature failure due to rust and degradation. |
| Inadequate surface preparation before welding. | Ensure all surfaces to be welded are meticulously cleaned of oils, grease, and oxides to achieve strong, defect-free welds essential for high-pressure hydraulic systems. |
A: This 304 Stainless Steel Stock Sheet is manufactured from 304 Stainless Steel.
A: Hydraulic Manifold Blocks, Hydraulic Reservoir Fabrication, Pressure Vessel Components.
Conversion factor: 1 ft-lb ≈ 1.356 Nm
| Status | Mating Component | Standard | Torque Spec | Engineering Notes |
|---|---|---|---|---|
| No verified compatibility data found for this component. | ||||