This robust 304 stainless steel stock sheet offers exceptional corrosion resistance and durability, making it ideal for fabricating components in lubricating systems and other demanding industrial environments.
| Standard | ASME B18 |
| Material | 304 Stainless Steel |
| Finish | Black Oxide |
| Grade | N/A |
| Thickness | 0.290" |
| Length | 31" |
| Width | 44" |
Engineered for reliability and performance, this 0.290-inch thick sheet is manufactured from high-grade 304 stainless steel, renowned for its superior resistance to corrosion, oxidation, and a wide range of chemicals. Measuring 31 inches in length and 44 inches in width, it provides ample material for custom fabrication. Its non-magnetic properties and excellent formability allow for intricate designs and precise fitting in critical lubrication pathways, ensuring consistent performance and longevity in high-stress applications.
This component strictly adheres to the tolerances, material specifications, and quality benchmarks set by the world's leading industrial manufacturers.
1. Precisely cut the sheet to the required dimensions using appropriate metalworking tools. 2. Deburr all edges thoroughly to ensure a smooth finish and prevent material contamination. 3. Form or weld the sheet as per the design specifications for the lubrication system component.
| Standard System | Designation |
|---|---|
| ISO Equivalent | ISO 9001:2015 Mfg |
| DIN Equivalent | Industry Standard |
| Primary Standard | ASME B18 |
| Tensile Strength | 75,000 psi (515 MPa) |
| Yield Strength | 30,000 psi (205 MPa) |
| Elongation in 2 in. | 40% min |
| Hardness | Rockwell B95 max |
| Carbon (C) | 0.08% max |
| Chromium (Cr) | 18.0 - 20.0% |
| Nickel (Ni) | 8.0 - 10.5% |
| Manganese (Mn) | 2.00% max |
| Size / Type | Est. Weight (lbs/100) | Shipping Weight (kg) |
|---|---|---|
| Standard | Varies by dimension | Contact Sales |
| Environment | Rating |
|---|---|
| Indoor / Dry | Excellent |
| Outdoor / Exposed | Excellent |
| Marine / Saltwater | Good |
| Chemical / Acidic | Not Recommended |
| ❌ Mistake | ✅ Correct Approach |
|---|---|
| Using standard carbon steel in corrosive lubrication environments. | Utilize 304 stainless steel for its inherent corrosion resistance, preventing premature failure and contamination. |
| Improperly cutting or deburring edges, leaving sharp fragments. | Always deburr edges meticulously after cutting to prevent metal particles from entering the lubrication system. |
A: This 304 Stainless Steel Stock Sheet is manufactured from 304 Stainless Steel.
A: Lubrication system components, Bearing housings, Oil containment trays, Sump fabrication.
Conversion factor: 1 ft-lb ≈ 1.356 Nm
| Status | Mating Component | Standard | Torque Spec | Engineering Notes |
|---|---|---|---|---|
| No verified compatibility data found for this component. | ||||