This 304 stainless steel stock sheet, precisely manufactured to 0.052" thickness, 14" width, and 46" length, is engineered for demanding abrading and polishing tasks. Its superior surface finish and corrosion resistance ensure optimal performance.
| Standard | ASME B18 |
| Material | 304 Stainless Steel |
| Finish | Passivated |
| Grade | N/A |
| Thickness | 0.052" |
| Length | 14" |
| Width | 46" |
Manufactured under strict quality controls, this 304 stainless steel stock sheet offers a nominal thickness of 0.052 inches, a width of 46 inches, and a length of 14 inches. Composed of 18% chromium and 8% nickel, this austenitic stainless steel provides excellent corrosion resistance and formability, making it ideal for applications requiring a smooth, defect-free surface. Its robust composition ensures durability and longevity in abrasive environments. The sheet is specifically intended for use in polishing and finishing processes where material integrity and surface quality are paramount.
This component strictly adheres to the tolerances, material specifications, and quality benchmarks set by the world's leading industrial manufacturers.
1. Ensure the work surface is clean and free from debris. 2. Position the stainless steel sheet carefully for the intended application. 3. Secure the sheet as per specific operational requirements.
| Standard System | Designation |
|---|---|
| ISO Equivalent | ISO 9001:2015 Mfg |
| DIN Equivalent | Industry Standard |
| Primary Standard | ASME B18 |
| Tensile Strength | 75,000 psi (515 MPa) |
| Yield Strength | 30,000 psi (205 MPa) |
| Elongation in 2 in. | 40% min |
| Hardness | Rockwell B95 max |
| Carbon (C) | 0.08% max |
| Chromium (Cr) | 18.0 - 20.0% |
| Nickel (Ni) | 8.0 - 10.5% |
| Manganese (Mn) | 2.00% max |
| Size / Type | Est. Weight (lbs/100) | Shipping Weight (kg) |
|---|---|---|
| Standard | Varies by dimension | Contact Sales |
| Environment | Rating |
|---|---|
| Indoor / Dry | Excellent |
| Outdoor / Exposed | Excellent |
| Marine / Saltwater | Good |
| Chemical / Acidic | Not Recommended |
| ❌ Mistake | ✅ Correct Approach |
|---|---|
| Using excessive force during polishing, leading to premature wear or surface damage. | Apply consistent, moderate pressure and utilize appropriate polishing media for the specific grade of stainless steel. |
| Not cleaning the sheet thoroughly before and after use, causing contamination. | Employ degreasers and non-abrasive cleaning agents to maintain surface integrity and prevent cross-contamination. |
A: This 304 Stainless Steel Stock Sheet is manufactured from 304 Stainless Steel.
A: Surface finishing and polishing of metal components, Preparation for plating or coating processes, Fabrication of decorative or functional metal surfaces.
Conversion factor: 1 ft-lb ≈ 1.356 Nm
| Status | Mating Component | Standard | Torque Spec | Engineering Notes |
|---|---|---|---|---|
| No verified compatibility data found for this component. | ||||