This 304 stainless steel stock sheet is engineered for superior performance in abrading and polishing tasks. Its precise dimensions and material integrity ensure consistent results and long-lasting durability in demanding environments.
| Standard | DIN 933 |
| Material | 304 Stainless Steel |
| Finish | Passivated |
| Grade | N/A |
| Thickness | 0.020" |
| Length | 45" |
| Width | 32" |
Built to exacting engineering tolerances, this 304 stainless steel stock sheet measures 0.020 inches in thickness, 45 inches in length, and 32 inches in width. Fabricated from AISI 304 (18-8) stainless steel, it offers excellent corrosion resistance, formability, and weldability. The inherent toughness of this austenitic alloy makes it ideal for applications requiring abrasion resistance and a high-quality polished finish, such as in food processing equipment, architectural components, and precision tooling.
This component strictly adheres to the tolerances, material specifications, and quality benchmarks set by the world's leading industrial manufacturers.
1. Ensure the work area is clean and free of debris. 2. Carefully unroll or position the sheet, avoiding sharp bends. 3. Secure the sheet using appropriate clamping mechanisms for the intended fabrication process.
| Standard System | Designation |
|---|---|
| ISO Equivalent | ISO 9001:2015 Mfg |
| DIN Equivalent | Industry Standard |
| Primary Standard | DIN 933 |
| Tensile Strength | 75,000 psi (515 MPa) |
| Yield Strength | 30,000 psi (205 MPa) |
| Elongation in 2 in. | 40% min |
| Hardness | Rockwell B95 max |
| Carbon (C) | 0.08% max |
| Chromium (Cr) | 18.0 - 20.0% |
| Nickel (Ni) | 8.0 - 10.5% |
| Manganese (Mn) | 2.00% max |
| Size / Type | Est. Weight (lbs/100) | Shipping Weight (kg) |
|---|---|---|
| Standard | Varies by dimension | Contact Sales |
| Environment | Rating |
|---|---|
| Indoor / Dry | Excellent |
| Outdoor / Exposed | Excellent |
| Marine / Saltwater | Good |
| Chemical / Acidic | Not Recommended |
| ❌ Mistake | ✅ Correct Approach |
|---|---|
| Using excessive force during bending, which can lead to material fatigue or cracking. | Employ gradual bending techniques with appropriate tooling to maintain material integrity. |
| Inadequate surface preparation before polishing, resulting in an uneven or marred finish. | Thoroughly clean and degrease the surface, and use a progressive series of abrasives to achieve the desired polish. |
A: This 304 Stainless Steel Stock Sheet is manufactured from 304 Stainless Steel.
A: Surface preparation for finishing, Component fabrication for food-grade equipment, Customized abrasion-resistant parts.