This 0.094" thick 304 stainless steel stock sheet offers superior corrosion resistance and formability. Measuring 42" x 17", it's engineered for demanding industrial and fabrication applications where durability is paramount.
| Standard | ASME B18 |
| Material | 304 Stainless Steel |
| Finish | Plain |
| Grade | N/A |
| Thickness | 0.094" |
| Length | 42" |
| Width | 17" |
Built to exacting engineering tolerances, this 304 stainless steel stock sheet boasts a nominal thickness of 0.094 inches (2.39 mm), a length of 42 inches (1067 mm), and a width of 17 inches (432 mm). Composed of 18% chromium and 8% nickel, it provides exceptional resistance to oxidation and corrosion, making it suitable for harsh environments. The material's inherent strength and ductility allow for precise fabrication, welding, and forming, ensuring integrity in critical applications.
This component strictly adheres to the tolerances, material specifications, and quality benchmarks set by the world's leading industrial manufacturers.
1. Clean the mounting surface thoroughly to remove any debris or contaminants. 2. Position the stock sheet according to design specifications, ensuring proper alignment. 3. Secure the sheet using appropriate fastening methods such as welding, riveting, or mechanical fasteners, adhering to structural load requirements.
| Standard System | Designation |
|---|---|
| ISO Equivalent | ISO 9001:2015 Mfg |
| DIN Equivalent | Industry Standard |
| Primary Standard | ASME B18 |
| Tensile Strength | 75,000 psi (515 MPa) |
| Yield Strength | 30,000 psi (205 MPa) |
| Elongation in 2 in. | 40% min |
| Hardness | Rockwell B95 max |
| Carbon (C) | 0.08% max |
| Chromium (Cr) | 18.0 - 20.0% |
| Nickel (Ni) | 8.0 - 10.5% |
| Manganese (Mn) | 2.00% max |
| Size / Type | Est. Weight (lbs/100) | Shipping Weight (kg) |
|---|---|---|
| Standard | Varies by dimension | Contact Sales |
| Environment | Rating |
|---|---|
| Indoor / Dry | Excellent |
| Outdoor / Exposed | Excellent |
| Marine / Saltwater | Good |
| Chemical / Acidic | Not Recommended |
| ❌ Mistake | ✅ Correct Approach |
|---|---|
| Inadequate surface preparation leading to poor adhesion or compromised structural integrity. | Ensure the mounting surface is meticulously cleaned and free from oil, grease, or any particulate matter before installation. |
| Over-stressing the material during bending or forming operations, resulting in cracking or deformation. | Utilize proper bending radii and forming techniques, consulting material datasheets for optimal processing parameters to avoid material failure. |
A: This 304 Stainless Steel Stock Sheet is manufactured from 304 Stainless Steel.
A: Food Processing Equipment Linings, Chemical Processing Vessels, General Fabrication and Sheet Metal Work.